В наличии
3799159 | 200B(TD)040 WP1250TAPE
Характеристики
Рост
|
762 m | 2500 ft |
Цвет
|
Black |
Масса, нетто
|
702.413 kg/km | 472 lb/kft |
ISO 9001:2015
|
Designed, manufactured and/or distributed under this quality management system |
Характеристики
Рост
|
762 m | 2500 ft |
Цвет
|
Black |
Масса, нетто
|
702.413 kg/km | 472 lb/kft |
ISO 9001:2015
|
Designed, manufactured and/or distributed under this quality management system |
Product Type
|
Empty conduit |
Material Type
|
High density polyethylene (HDPE) | Polyester |
Product Brand
|
ConQuest® |
Conductor Type
|
Solid |
Nominal Size
|
2 in |
Conduit Type
|
Toneable |
Wall Type
|
Smooth |
Wall Thickness Designation
|
SCH 40 |
Density Test Method
|
ASTM D792A |
Density, maximum
|
0.955 g/cm³ | 0.035 lb/in³ |
Density, minimum
|
0.941 g/cm³ | 0.034 lb/in³ |
Design Standard
|
ASTM D3350-05 |
Inner Diameter, nominal
|
51.994 mm | 2.047 in |
Outer Diameter, nominal
|
60.325 mm | 2.375 in |
Wall Thickness, minimum
|
3.912 mm | 0.154 in |
Flexural Modulus, minimum
|
551.581 N/mm² | 80000 psi |
Flexural Property Test Method
|
ASTM D790 |
Hydrostatic Design Basis
|
Not pressure rated |
Hydrostatic Design Test Method
|
ASTM D2837 |
Melt Flow Rate Test Method
|
ASTM D1238 |
Melt Flow Rate, maximum
|
0.39 g/10 min |
Minimum Bend Radius, unsupported
|
660.4 mm | 26 in |
Tensile Property Test Method
|
ASTM D638 |
Tensile Strength at yield, minimum
|
20.684 N/mm² | 3000 psi |
Breaking Strength
|
566.99 kg | 1250 lb |
Pull Line Type
|
Tape |
Pulling Tension, maximum
|
1043.262 kg | 2300 lb |
Environmental Stress Crack Resistance
|
Failure rate of 10% within 96 hours |
Environmental Stress Test Method
|
ASTM D1693, ESCR Condition B |
Conductor Elongation, maximum
|
30 % |
Conductor Diameter
|
1.024 mm | 0.0403 in |
Conductor Gauge
|
18 AWG |
Conductor Resistance
|
98.425 ohms/km | 30 ohms/kft |
Conductor Material Type
|
Copper-clad steel (CCS) |
Conductor Tensile Strength, minimum
|
344.738 N/mm² | 50000 psi |
Pulling Tension Note
|
Applies to products manufactured after December 31, 2012 |